Antimicrobial gels

ABSTRACT

The present invention pertains to antimicrobial compositions comprising inter alia at least one alkenyl- and/or alkynyl-substituted polysiloxane, at least one polysiloxane comprising silicon-bonded hydrogen atoms, and at least one hydrosilylation catalyst, as well as antimicrobial silicone gels, wound dressings, and methods of preparing the above.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a U.S. National Phase Application ofInternational Application No. PCT/SE2011/050452, filed Apr. 13, 2011,which claims priority to Swedish Patent Application No. 1050367-0, filedApr. 14, 2010, and U.S. Patent Application No. 61/323,926, filed Apr.14, 2010, all of which applications are incorporated herein fully bythis reference.

TECHNICAL FIELD

The present invention pertains to antimicrobial gel-formingcompositions, antimicrobial silicone gels, and antimicrobial wounddressings comprising the antimicrobial silicone gels, as well as methodsof preparing the above.

TECHNICAL BACKGROUND

The increasing prevalence of microbial strains exhibiting multidrugresistance as well as the surging pressure on healthcare systemsworldwide have resulted in a veritable escalation over recent decades ofnosocomial as well as community-acquired infections. Patients undergoingmajor surgical procedures, implantation of or interaction with medicaldevices, or patients with severe burns or chronic wounds, areparticularly susceptible to microbial, notably bacterial and fungal,infections. Methicillin-resistant Staphylococcus aureus, Pseudomonasaeruginosa, as well as various yeast species of the genus Candida, arecommonly associated with infected wounds and burns, often resulting insevere and complicated infections, placing additional burden on thehealthcare system and on an already distressed patient.

Hygiene measures applied in healthcare settings, such as isolation ofinfected patients, improved surface sanitation, and the use of alcoholrubs and gels, undoubtedly mitigate the above problems to a certainextent, but adequate and efficacious wound care is a paramountdeterminant for preventing initial microbial colonization and subsequentspread of infectious diseases. Conventional wound dressings have longproved insufficient for treating, inter alia, severe burns and chronicwounds, with the implication that various types of antimicrobialdressings have been developed, comprising inter alia conventionalantiseptics, antibiotics, antimicrobial peptides, or metallic agentswith antimicrobial properties.

EP1274473, for instance, discloses antimicrobial coatings for wounddressings comprising a bioadsorbable substrate associated with one ormore antimicrobial metals that releases said antimicrobial agent uponcontact with an alcohol or water-based electrolyte. The bioadsorbablepolymer is selected from a group comprising inter alia polyglycolicacid, glycolide, lactic acid, lactide, proteins, or polysaccharides.

The inherent antimicrobial properties of certain silver-containingcompounds are being explored in various types of wound dressings.WO2002062403, inter alia, teaches a medical dressing comprising acomplex of silver and being capable of releasing antimicrobial silverion activity. More specifically, the silver complex comprises acombination of silver and a Group IV transition element, preferablyzirconium, in order to enable controlled release of the silver ion to awound bed.

US20030036717 describes an elastic compress consisting of an elastomericmatrix highly plasticized with a non-polar oil and containing adispersed hydrocolloid. The compress additionally comprises at least oneantiseptic agent, for instance a silver salt, and at least onesurfactant for improving the bioavailability of the antiseptic agent.

Silicones are commonly utilized in various types of medical devices andin particular in wound dressings, as a result of its favourableintrinsic properties. Unlike many other materials used in wounddressings and medical devices, silicones possess attractivecharacteristics pertaining to inter alia manufacturing advantages,cohesion, tack, and adhesion, implying that they often constitute thematerials of choice for wound dressing applications. WO1993019710discloses an absorbent wound dressing comprising a layer of hydrophobicsilicone gel, a layer of carrier material, and an absorbent body,providing a soft wound dressing having favourable properties relating toadhesive strength, ease of removal, and leakage prevention.

WO2008057155 discloses silicone gel forming compositions for temporarilyadhering a medical device to a biological substrate, such as skin. Saiddisclosure teaches silicone gel compositions comprising active agents,for instance antibiotics, antiseptics, antifungals, anti-inflammatoryagents, hormones, anticancer agents, histamine blockers, beta blockers,vitamins, sedatives, analgesics, proteolytic enzymes, and peptides,which can be bound in the composition. Further, WO2008057155incidentally teaches including silver and derivatives as active agentsthat can be bound in the composition, but information about theparameters governing therapeutic efficacy, as well as efficacyvalidation, is largely absent.

SUMMARY OF THE INVENTION

It is hence an object of the present invention to overcome theabove-identified problems and satisfy the existing needs within the art,i. e. to provide for facile and efficient manufacture of antimicrobialsilicone-based compositions, gels, and wound dressings, as well ascompositions, gels, and wound dressings per se having antimicrobialproperties for adequate and efficacious wound treatment, through releaseof antimicrobial silver-containing compounds, in particular silver saltsand/or silver ions. Thus, the present invention pertains toantimicrobial compositions, antimicrobial gels, and antimicrobialdressings, as well as methods for the preparation of said antimicrobialgels and dressings, and various uses thereof.

More specifically, the present invention relates to antimicrobialcompositions comprising at least one alkenyl- and/or alkynyl-substitutedpolydiorganosiloxane, at least one polysiloxane comprisingsilicon-bonded hydrogen atoms and at least one hydrosilylation catalyst,wherein said composition further comprises at least one silver salt andat least one hydrophilic component (which may enhance silver release)that exerts a swelling effect, as well as antimicrobial gels producedfrom said antimicrobial composition through crosslinking the at leastone alkenyl- and/or alkynyl-substituted polysiloxane and the at leastone polysiloxane comprising silicon-bonded hydrogen atoms (i.e. Si—Hmoieties). Additionally, the invention pertains to further aspectsrelating to antimicrobial gels, inter alia prepared from compositions inaccordance with the present invention, for instance through curing, aswell as antimicrobial dressings comprising said antimicrobial gels. Theantimicrobial gels as per the present invention may be formed bycreating at least one covalent bond between at least one alkenyl and/oralkynyl moiety of a first polysiloxane and at least one Si—H moiety ofsecond polysiloxane, said antimicrobial gel further comprising at leastone hydrosilylation catalyst, wherein said antimicrobial gel furthercomprises at least one silver salt, and at least one (optionally silverrelease-enhancing) hydrophilic component that makes said antimicrobialgel swell at least 5% (wt/wt) after 24 hours in Solution A, as measuredby the free swell absorption method.

Moreover, further aspects of the present invention pertain to methods ofpreparing said antimicrobial gels and dressing, comprising inter aliathe steps of preparation of three mixtures, either simultaneously orsequentially or in any combinations of preparations. Said three mixturesmay comprise (i) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one hydrosilylation catalyst and, optionally,silica particles, (ii) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one CE and/or at least one CL, and, optionally,silica particles, and (iii) at least one silver salt and at least onesiloxane-containing copolymer. Subsequently, at least one silver-releaseenhancing hydrophilic component is mixed with mixture (i) and/or mixture(ii), followed by optionally heating the obtained mixture(s) to whichthe silver-release enhancing hydrophilic component was added, in orderto melt the silver-release enhancing hydrophilic component. Theresulting mixtures are thereafter mixed and, after optional coating of asuitable substrate, cured, thus creating either an antimicrobial geland/or an antimicrobial dressing, in accordance with the presentinvention.

The present invention thus provides antimicrobial compositions, gels,and dressings having substantially improved properties compared to theantimicrobial products for wound treatment constituting the current art.The presence of silver-containing compounds, such as silver salts and/orsilver ions, and (optionally silver release-enhancing) hydrophiliccomponents in the compositions, as well as in the gels and dressings,confer antimicrobial properties not only to the products per se, butalso imply that the silver salts/ions can exert antimicrobial effects insurrounding areas.

Further, the silver release can be modulated through the use of variousdifferent hydrophilic components that causes the compositions and gelsto swell, thereby enhancing the inflow of liquid and the dispersions anddistribution of the silver compounds, implying that the antimicrobialproducts and their intrinsic effects can be adapted to suit specifictherapeutic purposes, for instance adjustment of the antimicrobialeffects depending on the type and nature of wound/burn/injury to betreated, or depending on the infectious agent in question. Additionally,as an implication of the optimized physical and chemical propertiesresulting from the presence of various types of additives andexcipients, inter alia siloxane-containing copolymers, silica particles,and siloxane polymer networks, the patient compliance and comfort, andconsequently the antimicrobial efficacy, is optimized.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 portrays a flow chart describing the various steps associatedwith an exemplary manufacturing method for antimicrobial gels and/ordressings.

FIG. 2 illustrates a flow chart describing the various steps associatedwith an exemplary laboratory-scale preparation method for antimicrobialgels and dressings.

FIG. 3 illustrates the reduction of P. aeruginosa and S. aureus afterexposure to the antimicrobial gels, and in particular formulation 5N6disclosed below, of the present invention.

FIG. 4 illustrates the reduction of P. aeruginosa after exposure toselected antimicrobial gels of the present invention.

FIG. 5 illustrates the importance (for enhancing silver release) of thehydrophilic component (silver release is expressed in % of the totaladded mass of Ag₂SO₄ at 24 h and 48 h (from various samples in NaNO₃solution)). The samples denoted 2N1 and 2N2 do not contain any (silverrelease-enhancing) hydrophilic component, as can be seen from Table 5.

DETAILED DESCRIPTION OF THE INVENTION

The present invention pertains inter alia to antimicrobial compositionsthat inhibit microbial growth, antimicrobial gels, produced inter aliafrom said compositions, various types of dressings comprising theantimicrobial gels for inhibiting microbial growth, as well as the useof the antimicrobial gels in various types of products for treatingwounds and inhibiting microbial growth.

Where features, embodiments, or aspects of the present invention aredescribed in terms of Markush groups, a person skilled in the art willrecognize that the invention is also thereby described in terms of anyindividual member or subgroup of members of the Markush group. Theperson skilled in the art will further recognize that the invention isalso thereby described in terms of any combination of individual membersor subgroups of members of Markush groups. Additionally, it should benoted that embodiments and features described in connection with one ofthe aspects and/or embodiments of the present invention also applymutatis mutandis to all the other aspects and/or embodiments of theinvention. For example, the at least one hydrophilic component (whichmay enhance silver release) described in connection with theantimicrobial compositions may naturally also be included in theantimicrobial gels, the excipients described in connection with theantimicrobial gels may also be comprised in the antimicrobialcompositions, the at least one silver salt as well as the concentrationof the at least one silver salt described in connection with theantimicrobial compositions naturally also apply to the antimicrobialgels, and the antimicrobial effects described in connection with acertain aspect and/or embodiment relating to a certain antimicrobial gelmay also be exerted by other antimicrobial gels, all in accordance withthe present invention.

A first aspect of the present invention relates to antimicrobial,silicone gel-forming compositions inhibiting microbial growth, whereinthe compositions comprise at least one alkenyl- and/oralkynyl-substituted polysiloxane, at least one polysiloxane comprisingsilicon-bonded hydrogen atoms, and at least one hydrosilylationcatalyst, wherein said composition further comprises at least one silversalt and at least one (optionally silver release-enhancing) hydrophiliccomponent, and wherein said at least one hydrophilic component makessaid antimicrobial composition, when cross-linked, swell at least 5%(wt/wt) after 24 hours in Solution A, as measured by the free swellabsorption method. In further embodiments as per the present invention,the swelling may be at least 10% (wt/wt) after 24 hours in Solution A,or at least 20% (wt/wt) after 24 hours in Solution A, or at least 20%(wt/wt) after 24 hours in Solution A, or at least 30% (wt/wt) after 24hours in Solution A, or at least 40% (wt/wt) after 24 hours in SolutionA, or at least 50% (wt/wt) after 24 hours in Solution A, or at least 75%(wt/wt) after 24 hours in Solution A, or at least 100% (wt/wt) after 24hours in Solution A, or at least 150% (wt/wt) after 24 hours in SolutionA, or at least 200% (wt/wt) after 24 hours in Solution A, or at least300% (wt/wt) after 24 hours in Solution A, or at least 400% (wt/wt)after 24 hours in Solution A, or at least 500% (wt/wt) after 24 hours inSolution A, or at least 600% (wt/wt) after 24 hours in Solution A, or atleast 700% (wt/wt) after 24 hours in Solution A or at least 800% (wt/wt)after 24 hours in Solution A or any other lower or higher value, and anyinterval created by the above figures e.g. from 5% (wt/wt) to 800%(wt/wt) after 24 hours in Solution A.

Optionally, the swelling may be measured at different time points, forinstance at 48 hours or at 72 hours, and also at these time points theswelling may be at least 10% (wt/wt) after 24 hours in Solution A, or atleast 20% (wt/wt) after 24 hours in Solution A, or at least 20% (wt/wt)after 24 hours in Solution A, or at least 30% (wt/wt) after 24 hours inSolution A, or at least 40% (wt/wt) after 24 hours in Solution A, or atleast 50% (wt/wt) after 24 hours in Solution A, or at least 75% (wt/wt)after 24 hours in Solution A, or at least 100% (wt/wt) after 24 hours inSolution A, or at least 150% (wt/wt) after 24 hours in Solution A, or atleast 200% (wt/wt) after 24 hours in Solution A, or at least 300%(wt/wt) after 24 hours in Solution A, or at least 400% (wt/wt) after 24hours in Solution A, or at least 500% (wt/wt) after 24 hours in SolutionA, or at least 600% (wt/wt) after 24 hours in Solution A, or at least700% (wt/wt) after 24 hours in Solution A or at least 800% (wt/wt) after24 hours in Solution A or any other lower or higher value, and anyinterval created by the above figures e.g. from 5% (wt/wt) to 800%(wt/wt) after 24 hours in Solution A.

The free swell absorption method employing Solution A is a standardmethodology used within the field for assessing swelling capacity. Thefree swell method is described in more detail below, but briefly theassay encompasses placing a pre-weighed dressing sample in a quantity oftest solution (in this case, Solution A) which is 40 times the mass ofthe sample. The sample is then allowed to absorb Solution A for aspecific time at a specific temperature, after which the sample isweighed again, in order to determine the free swell absorption capacity.

The silver compounds and/or salts endow the composition withantimicrobial properties, whereas the release-enhancing hydrophiliccomponent promotes efficient release of the silver salt, therebyenhancing the antimicrobial efficacy of the composition. Without wishingto be bound by any particular theory, it is surmised that the presenceof at least one hydrophilic component exhibiting a certain free swell inthe antimicrobial composition increases the solubilization, thedispersion, and the inflow of liquid into the composition, therebyincreasing the release of silver and increasing the antimicrobialproperties of the composition.

The at least one polysiloxane comprising silicon-bonded hydrogen atomsmay, as is well-known within the art, comprise inter alia at least onechain extender (CE) and/or at least one crosslinker (CL). Chainextenders generally comprise polysiloxanes having hydrogen atomsattached to terminal silicon-atoms, whereas crosslinkers normallycomprise polysiloxanes having hydrogen-substituted silicon atomscovalently bound only to the internal, non-terminal silicon atoms. Bothbranched and linear polysiloxanes having various different chemicalnatures as well as various viscosities may be utilized in accordancewith the present invention. The at least one alkenyl- and/oralkynyl-substituted polydiorganosiloxane and the at least onepolysiloxane comprising silicon-bonded hydrogen atoms may have hydrogenor various hydrocarbon substituents, such as saturated or unsaturated,branched or linear, C₁-C₂₀, preferably C₁-C₅, hydrocarbon chains,optionally with heteroatoms present. In accordance with the aspects andembodiments of the present invention, said organic substituents maycomprise methyl, ethyl, propyl, butyl, vinyl, allyl, and/or aryl, andcombinations of these, in any suitable position, for instance as pendantor terminal groups. The term “alkenyl- and/or alkynyl-substitutedpolysiloxane” is to be understood as comprising polydiorganosiloxanessubstituted with groups comprising unsaturated carbon-carbon bonds, i.e.both carbon-carbon double bonds and/or carbon-carbon triple bonds. Thus,the term “alkenyl- and/or alkynyl-substituted polysiloxane” shall beunderstood as comprising both alkenyl-substituted polysiloxanes as wellas alkynyl-substituted polysiloxanes, as well as alkenyl andalkynyl-substituted polysiloxanes. Further, the term “when cross-linked”shall be understood to relate to the cross-link that can be createdbetween alkenyl and/alkynyl moieties (i.e. unsaturations) of at leastone polysiloxane and the Si—H moiety of a second polysiloxane.Additionally, the term “polysiloxane” shall be understood to pertain toall types of polysiloxanes, for instance polydiorganosiloxanes, etc.,and within the context of the present invention, these two terms areused interchangeably. Finally, the process feature of “mixing mixture(i) and mixture (ii)” shall be understood to relate to mixing themixture remaining after the preceding method step (i.e. the mixture thatwas not mixed with mixture (iii)) with the mixture obtained in theprevious step (i.e. with mixture (iii) combined with either mixture (i)and/or mixture (ii)).

Further in accordance with the aspects and embodiments of the presentinvention, it is important that moieties capable of crosslinking the atleast one alkenyl- and/or alkynyl-substituted polysiloxane and the atleast one polysiloxane comprising silicon-bonded hydrogen atoms (i.e. anSi—H moiety), upon reacting said components, are present, in order tomediate formation of silicone gels. Mechanisms within the presentinvention for reacting, and thereby crosslinking, the at least onealkenyl- and/or alkynyl-substituted polysiloxane and the at least onepolysiloxane comprising silicon-bonded hydrogen atoms compriseshydrosilylation, in which a polysiloxane having an Si—H reactive groupreacts with a polysiloxane (polydiorganosiloxane) having analiphatically unsaturated reactive group, in the presence of ahydrosilylation catalyst, typically Pt and/or Pd. Typical silicone gelforming compositions include alkenyl- and/or alkynyl-functionalpolyorganosiloxanes (e.g. vinyl functional polyorganosiloxanes),α,ω-hydrogen polyorganosiloxanes, i. e. chain extenders,hydrogen-functional polyorganosiloxanes, i. e. cross-linkers, and ahydrosilylation catalyst (e.g. a platinum complex).

Further in line with the present invention, the viscosities of the atleast one alkenyl- and/or alkynyl-substituted polydiorganosiloxane andthe at least one polysiloxane comprising silicon-bonded hydrogen atomsmay vary in accordance with the desired properties of the resultantantimicrobial gels and dressings, in accordance with the aspects and theembodiments of the invention. As per an embodiment of the presentinvention, a mixture of the at least one alkenyl- and/oralkynyl-substituted polydiorganosiloxane and the at least onepolysiloxane comprising silicon-bonded hydrogen atoms may have aviscosity at ambient temperature and 1 atmosphere between 500 and100,000 cSt, preferably between 500 and 20,000 cSt, prior to theaddition of any additives and/or excipients, and before cross-linking ofthe at least one alkenyl- and/or alkynyl-substitutedpolydiorganosiloxane and the at least one polysiloxane comprisingsilicon-bonded hydrogen atoms.

In one embodiment of the present invention, the at least one (optionallysilver release-enhancing) hydrophilic component may inter alia beselected from the group comprising mono- di- and/or polysaccharides,sugar alcohols, polyols, polyethers, polyesters, polyamides and/orpolymers comprising pendant carboxylic acid groups and/or pendantsulphonate groups, but other hydrophilic polymers and molecules are alsowithin the scope of the invention. In a further embodiment, the at leastone hydrophilic component may for instance be selected from the groupcomprising glucose, xylitol, sorbitol, mannitol, cyclodextrins,cellulose, hemicellulose, carboxymethylated cellulose, chitosan,dextran, chitin, amylose, amylopectin, polyethylene glycol,polypropylene glycol, copolymers of polyethylene glycol andpolypropylene glycol, polyglycerol, poly(acrylic acid), copolymers ofacrylic acid and C₁₀-C₃₀ alkyl acrylate, poly(acrylamide), maleicanhydride polymers and copolymers, carboxy methyl cellulose, methylcellulose, hydroxymethylpropylcellulose, ethylcellulose,carboxyethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose,carboxymethylcellulose, cellulose alkyl sulfonate, polystyrenesulphonates, vinyl acids and vinyl alcohols. In yet another embodiment,the hydrophilic component is preferably present in a concentration thatranges from approximately 3% to 40% (w/w), and more preferably from 4%to 30%.

In a further embodiment, numerous different types of silver salts withantimicrobial properties are within scope of the present invention, andthe at least one silver salt may thus for instance be selected from thegroup comprising Ag₂SO₄, Ag₂SO₃, AgNO₃, Ag₂CO₃, Ag₃PO₄, silverzirconium, and/or organic silver salts, such as silver citrate, silveracetate, silver lactate and/or combinations or mixtures thereof. Variousother compounds providing silver ions are conceivable and such compoundsare also within the spirit of the present invention. In an embodiment ofthe present invention, the silver salt concentration may range fromapproximately 1% to 30%, and preferably from approximately 2% to 20%. Asthe silver salt is the primary antimicrobial agent bestowing thecomposition with its antimicrobial properties, it is conceivable that anincreasing silver concentration would correspond to an improved overallantimicrobial effect. However, without wishing to be bound by anyparticular theory, it is surmised that it may potentially also beessential to provide compositions and gels with optimized combinationsof silver release properties and silver salt concentration, asillustrated by the efficacy of the antimicrobial compositions and gelsof the present invention. Nevertheless, other aspects and embodiment ofthe present invention may also contribute the antimicrobial properties.

In order to further improve the antimicrobial and overall properties ofthe antimicrobial composition, further embodiments of the presentinvention relate to compositions that may comprise at least onesiloxane-containing copolymer selected from the group comprising atleast one siloxane polymer network and at least one siloxane polyether(SPE). The at least one siloxane polymer network may comprise forinstance at least one cross-polymer and/or at least one ter-polymer.SPEs are block copolymers with segments comprising polysiloxane (forinstance PDMS) and additional segments containing at least one type ofpolyether, for instance polyethyleneglycol (PEG) or polypropylenglycol(PPG). Suitable SPEs may for instance be selected from the groupcomprising bis-isobutyl PEG/PPG-10/7 dimethicone copolymer (Dow CorningToray FZ 2233) and Silwet 8500 (from Momentive).

In yet another embodiment, the siloxane polymer network may for instancebe present at a concentration of between approximately 2% and 30%,preferably between 5% and 20%, and it may, in accordance with anadditional embodiment, for instance be selected from the groupcomprising poly-ether-siloxane copolymer networks,cyclopentasiloxane-alkyl cetearyl dimethicone copolymer networks(Velvesil 125), and vinyldimethyl/trimethylsiloxysilicate stearyldimethicone crosspolymer.

Polydimethylsiloxane (PDMS) copolymers, i.e. suitablesiloxane-containing polymers in accordance with the present invention,consist of at least two different polymer types, which are arranged inblocks of PDMS and the other polymer, for example polyethylene oxide.When three different polymer components are present in the same polymer,it is termed a terpolymer. Common architectures of copolymers arelinear, where the at least two different blocks are arranged in series,or graft copolymers, where for example PEO is grafted along a PDMSbackbone, resembling a comb. The relative abundance of the PDMS and theother polymer components will determine properties such ashydrophilicity, which is one of the desirable properties as per thepresent invention. The co- and terpolymers may also be intramolecularlycrosslinked, in which case the polymers form a network (sometimes termedcrosspolymer). Said network may be swollen in solvents, for examplecyclic siloxanes to form a gel, with advantages relating to for instanceease of processing, in spite of the crosslinked polymer itself havingvery high viscosity.

In further embodiments of the present invention, the antimicrobialcompositions and gels may comprise particles for facilitating and/orenabling the dispersion of constituents of the composition, primarilycertain silver-release enhancing hydrophilic components but potentiallyalso the antimicrobial silver salts. As per an embodiment of the presentinvention, particles conceivable within the scope of the invention mayfor instance be silica particles, but other suitable particles are alsowithin the scope of the present invention. The particles may be presentin a concentration ranging from 2 to 5%, preferably between 2 to 3%. Inaccordance with another embodiment of the present invention, theantimicrobial composition may further comprise at least onesiloxane-containing copolymer. Said siloxane-containing copolymer mayfor instance comprise a hydrophilic polymer, such as PEG or PPG, orother polymers known to a person skilled in the art.

In yet other embodiments of the antimicrobial compositions of thepresent invention, the at least one alkenyl- and/or alkynyl-substitutedpolydiorganosiloxane may be covalently crosslinked to the at least onepolysiloxane comprising silicon-bonded hydrogen atoms, thereby formingan antimicrobial gel.

A second aspect of the present invention pertains to antimicrobial gelscomprising at least one alkenyl- and/or alkynyl-substituted polysiloxane(polydiorganosiloxanes) covalently bound to at least one polysiloxanecomprising silicon-bonded hydrogen atoms, said antimicrobial gel furthercomprising at least one hydrosilylation catalyst, characterized in thatsaid antimicrobial gel further comprises at least one silver salt, andat least one (optionally silver release-enhancing) hydrophiliccomponent. Said antimicrobial gels may, inter alia, be produced from thecompositions of the present invention, for instance through crosslinkingthe at least one alkenyl- and/or alkynyl-substituted polysiloxane andthe at least one polysiloxane having silicon-bonded hydrogen atoms. Thecrosslinking may be effected through reacting the at least one alkenyl-and/or alkynyl-substituted polysiloxane and the at least onepolysiloxane having silicon-bonded hydrogen atoms, for instance using,in an embodiment of the present invention, curing. Curing may be carriedout under a various different conditions depending on the components ofthe composition, as well as on the desired properties of the resultantgel. In an additional embodiment, the curing may inter alia be carriedout at between 40 and 140 degrees Centigrade, preferably between 60 and130 degrees. In yet another embodiment, the timeframe during which thecuring reaction is carried out may also vary depending on the abovefactors, but the crosslinking curing reaction may for instance becarried out for between 5 seconds and 2 hours, preferably between 10seconds and 30 minutes, and more preferably between 30 seconds and 2minutes.

In yet another embodiment as per the present invention, theantimicrobial gel may further comprise one or more excipients, forinstance selected from siloxane-containing copolymers, siloxane polymernetworks, and silica particles.

In a further embodiment, the antimicrobial gels of the present inventionmay comprise numerous different types of silver salts. Said silver saltmay thus for instance be selected from the group comprising Ag₂SO₄,Ag₂SO₃, AgNO₃, Ag₂CO₃, Ag₃PO₄, silver zirconium, and/or organic silversalts, such as silver citrate, silver acetate, silver lactate and/orcombinations or mixtures thereof. Various other compounds providingsilver ions are conceivable and such compounds are also within thespirit of the present invention. In an embodiment of the presentinvention, the silver salt concentration may range from approximately 1%to 30%, and preferably from approximately 2% to 20%.

In an additional embodiment of the present invention, the antimicrobialgels of the present invention may comprise at least one (silverrelease-enhancing) hydrophilic component, inter alia selected from thegroup comprising mono- di- and/or polysaccharides, sugar alcohols,polyols, polyethers, polyesters, polyamides and/or polymers comprisingpendant carboxylic acid groups and/or pendant sulphonate groups, butother hydrophilic polymers and molecules are also within the scope ofthe invention. In a further embodiment, the at least one hydrophiliccomponent, which may enhance silver release, may for instance beselected from the group comprising glucose, xylitol, sorbitol, mannitol,cyclodextrins, cellulose, hemicellulose, carboxymethylated cellulose,chitosan, dextran, chitin, amylose, amylopectin, polyethylene glycol,polypropylene glycol, copolymers of polyethylene glycol andpolypropylene glycol, polyglycerol, poly(acrylic acid), copolymers ofacrylic acid and C₁₀-C₃₀ alkyl acrylate, poly(acrylamide), maleicanhydride polymers and copolymers, carboxy methyl cellulose, methylcellulose, hydroxymethylpropylcellulose, ethylcellulose,carboxyethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose,carboxymethylcellulose, cellulose alkyl sulfonate, polystyrenesulphonates, vinyl acids and vinyl alcohols. In yet another embodiment,the (silver release-enhancing) hydrophilic component is preferablypresent in a concentration that ranges from approximately 3% to 40%(w/w), and more preferably from 4% to 30%.

The silver-releasing properties of the antimicrobial gels naturally havea significant impact on the overall antimicrobial effects seen whenutilizing the gel and other aspects of the present invention in forinstance a clinical setting. The amount of silver ions released from theprototypes may be investigated, in accordance with embodiments of thepresent invention, using a test method based on measurements of silverrelease from an antimicrobial gel and/or an antimicrobial wounddressing, using a two-compartment model. A piece of the prototypegel/dressing (d=20 mm, area 3.14 cm²) was placed without release film onthe membrane of a cell culture insert (pore size 8.0 μm), placed in a6-well plate containing 4 mL sodium nitrate (NaNO₃, 0.15 M). The plateswere incubated at 35° C. and the silver ion concentration was determinedin the medium using a silver electrode. When the concentration was to bedetermined during several days, the samples were placed in fresh NaNO₃after each measurement. The total silver concentration may also bedetermined using atomic absorption spectroscopy (AAS), if the medium isnot compatible with the silver electrode (e.g. simulated wound fluid(SWF)), as well as other suitable methods.

As per one embodiment in line with the present invention, theantimicrobial gels may inhibit microbial growth, defined using interalia the corrected zone of inhibition (CZoI) or the two-compartment testmethods, over various time frames. The two-compartment test methodinvolves culturing bacteria in 6-well plates, and, when evaluating theantimicrobial efficacy, placing dressing pieces (20 mm) in co-cultureinserts (the porous membrane in the cell culture insert is detached sothat the dressing has full contact with the bacterial culture). Bacteriaare cultured in chemical simulated wound fluid, cSWF (NaCl 2.922 g,NaOHCO3 1.68 g, KCl 0.149 g, COCl2×2H2O 0.184 g, bovine albumin 16.5 g,in 500 ml Super Q water, pH 8.49. Initial concentration of the testorganism is approximately 10⁶ CFU/ml prior to adding the test sample.The plates are incubated with agitation (100 rpm) and samples arewithdrawn after specified times. The number of viable counts of the testorganism is determined with standard surface plate count method and theamount of antimicrobials released is analyzed with relevant methodology,e.g. atomic absorption spectroscopy (AAS) for heavy metals. For releasestudies, the method can be used only with desired test fluid and nobacteria present.

The CZoI method involves placing a piece of wound dressing (d=20 mm) onan agar surface (Muller Hinton agar (MH agar)) in 25 ml/9 cm plates thatproduce an agar depth of 4 mm, which has been seeded with the testmicroorganism (Pseudomonas aeruginosa, ATCC 15442, and Staphylococcusaureus, ATCC 6538). Diffusion of antimicrobial agent into the agarresults in inhibition of growth, which appears as a clear zone on theagar. The corrected zone of inhibition is determined as the diameter ofthe whole inhibition zone minus the size of the dressing.

The CZoI associated with the antimicrobial gels of the present inventionmay be, inter alia, approximately at least 2 mm at 24 h andapproximately at least 2 mm at 48 h. Further in accordance with theinvention, the accumulated silver release from the antimicrobial gelsmay amount to at least 0.3% of the total silver content after 24 h, andat least 0.5% of the total silver content after 48 h. In furtherembodiments of the present invention, the antimicrobial effects mediatedby the antimicrobial gels of the present invention, as evaluated usingthe two-compartment model, may be in the order of at least one log,preferably at least two logs, and more preferably at least three logs.

An additional, standard method for evaluating the antimicrobial efficacyof the products as per the present invention is a modified version ofISO 22196:2007, i.e. a so called antimicrobial contact method. Briefly,the method encompasses covering a 5×5 cm sample piece with a thin layerof inoculum, incubating for a specific time period (commonly 24 h)before determining the number of viable test organisms. Test organismviability may be carried out as follows: shake method usingneutralization buffer, plating, incubation, and plate count method. Theminor deviations from the reference method in this case are that theinoculum used contains agar agar (3 g/l) and nutrient broth (5%). Thetest samples were inoculated with 1 ml inoculum containing approximately1.2-3.0×10⁶ CFU/ml.

Using the above-described, modified ISO method, the antimicrobialproducts of the present invention caused more than 3 log reductions inP. aeruginosa (ATCC 15442) viability.

The adhesion properties exhibited by the gel of the present inventionare naturally highly important both for the actual antimicrobialefficacy and for the patient comfort and compliance. Thus, in accordancewith the present invention, the antimicrobial gels may have an adhesionwith steel of between 0.1 and 2 N, preferably between 0.1 and 1 N, andmost preferably between 0.1 and 0.5 N. The determination of the adhesionis in this instance carried out in accordance with ASTM Internationals'standard D3330/D3330M-04, method F, but other suitable methods andstandards may also be utilized. The antimicrobial gel may be combinedwith or incorporated into a dressing prior to application to a patient,but it is also within the spirit of the invention to apply theantimicrobial gel directly to a patient in need thereof.

In further embodiments of the present invention, the antimicrobialsilicone gels of the present invention can be prepared in the form oflayers and/or surface having different thicknesses, morphologies,patterns, functionalities, or the like, using any suitable technique,for instance extruding, calendering, molding, brushing, spraying,casting, coating, and/or application by hand. In yet another embodiment,the silicone gel may be preformed by casting and curing the gel-formingantimicrobial composition on a substrate. In further embodiments as perthe invention, the layer and/or surfaces comprising the gel of thepresent invention may be in any geometric form, for instance dots,circles, networks, continuous configurations, discontinuousconfigurations, perforated layers and/or surfaces, and the like.

In accordance with further embodiments of the present invention, thesubstrate on which the antimicrobial gel is to be applied in order tocreate a wound dressing comprising the antimicrobial gel may be anysurface that will generate the desired properties. The substrate mayinter alia be selected from the group comprising inter alia a wounddressing, an ostomy dressing, ostomy baseplate, incision film, surgicaldrape, a patch, a bandage, a band-aid, a plaster, an adhesive, anadhesive tape, an adhesive plaster, a sticking-plaster, or acourt-plaster, and/or any combination thereof. Further, the substratemay also be a component for the manufacture of any one of the abovesubstrates and/or wound dressings, for instance a film, a textile, afoam, a non-woven film, a fiber network, a knitted fabric, or the like.Thus, in additional embodiments, the substrates and/or the wounddressings of the present invention may comprise textiles, films, foams,non-woven films, fiber networks, foams, knitted fabrics, and the like.

Suitable substrates in accordance with further embodiments of thepresent invention may comprise polyesters, polyethylenes,polypropylenes, polybutylenes, polymethylpentenes, polyolefins,polyvinyl acetates, polyvinyl chloride derivatives, polyethylene-vinylacetate (EVA) and its copolymers, polyvinyls, polyvinyl alcohol,polyvinylbutyral, polyvinyl formal, polyacrylonitrile, polyurethanes andpolyurethane-ureas, polystyrenes and their copolymers, epoxy andphenolic plastics, polyacrylic and polyacrylates derivatives,cellulose-based films, polyimides, polyamides, silicone elastomers,polyphenyl sulfide, polycarbonates, phenoplastes, fluorinated polymers,polyoxymethylenes, polyphenylene oxides, polysulfones,polysaccharide-based materials, and/or silicones, and/or any combinationthereof.

As per one further aspect, the present invention pertains to anantimicrobial gel wherein said antimicrobial gel is formed by creatingat least one covalent bond between at least one an alkenyl and/oralkynyl moiety of a first polysiloxane and at least one Si—H (i.e. asilicon-bonded hydrogen atom) moiety of second polysiloxane, saidantimicrobial gel further comprising at least one hydrosilylationcatalyst, at least one silver salt, and at least one (silverrelease-enhancing) hydrophilic component, wherein said at least onehydrophilic component makes said antimicrobial gel swell at least 5%(wt/wt) after 24 hours in Solution A, as measured by the free swellabsorption method. Further in accordance with additional embodiments asper the present invention, the swelling may be at least 10% (wt/wt)after 24 hours in Solution A, or at least 20% (wt/wt) after 24 hours inSolution A, or at least 20% (wt/wt) after 24 hours in Solution A, or atleast 30% (wt/wt) after 24 hours in Solution A, or at least 40% (wt/wt)after 24 hours in Solution A, or at least 50% (wt/wt) after 24 hours inSolution A, or at least 75% (wt/wt) after 24 hours in Solution A, or atleast 100% (wt/wt) after 24 hours in Solution A, or at least 150%(wt/wt) after 24 hours in Solution A, or at least 200% (wt/wt) after 24hours in Solution A, or at least 300% (wt/wt) after 24 hours in SolutionA, or at least 400% (wt/wt) after 24 hours in Solution A, or at least500% (wt/wt) after 24 hours in Solution A, or at least 600% (wt/wt)after 24 hours in Solution A, or at least 700% (wt/wt) after 24 hours inSolution A or at least 800% (wt/wt) after 24 hours in Solution A or anyother lower or higher value, and any interval created by the abovefigures e.g. from 5% (wt/wt) to 800% (wt/wt) after 24 hours in SolutionA.

Optionally, the swelling may be measured at different time points, forinstance at 48 hours or at 72 hours, and also at these time points theswelling may be at least 10% (wt/wt) after 24 hours in Solution A, or atleast 20% (wt/wt) after 24 hours in Solution A, or at least 20% (wt/wt)after 24 hours in Solution A, or at least 30% (wt/wt) after 24 hours inSolution A, or at least 40% (wt/wt) after 24 hours in Solution A, or atleast 50% (wt/wt) after 24 hours in Solution A, or at least 75% (wt/wt)after 24 hours in Solution A, or at least 100% (wt/wt) after 24 hours inSolution A, or at least 150% (wt/wt) after 24 hours in Solution A, or atleast 200% (wt/wt) after 24 hours in Solution A, or at least 300%(wt/wt) after 24 hours in Solution A, or at least 400% (wt/wt) after 24hours in Solution A, or at least 500% (wt/wt) after 24 hours in SolutionA, or at least 600% (wt/wt) after 24 hours in Solution A, or at least700% (wt/wt) after 24 hours in Solution A or at least 800% (wt/wt) after24 hours in Solution A or any other lower or higher value, and anyinterval created by the above figures e.g. from 5% (wt/wt) to 800%(wt/wt) after 24 hours in Solution A.

As abovementioned, the free swell absorption method is utilized todetermine the swell properties. The free swell absorption method iscarried out approximately as follows.

A suitable volume of Solution A is prepared. 1 liter is for instanceprepared according to the following protocol:

Dissolve 8.298 g of sodium chloride (NaCl) and 0.368 g of calciumchloride dihydrate (CaCl₂.H₂O) in deionised water and fill up to 1 literin a volumetric flask.

The first step of the free swell absorption method (which is a standardtest method denoted EN 13726-1) involves cutting or punching a testpiece of 5×5 cm of the product (for instance the antimicrobial gel) tobe tested. In case of cavity dressings, use 0.2 gram. Second, conditionthe test piece at 23±2° C. and (50±2) % RH and subsequently weigh thesample and place it in a Petri dish. Add a quantity of Solution A warmedto 37±1° C. corresponding to 40 times the mass of the sample, ±0.5 g.Transfer to the oven and allow it to stand for the selected time, e.g.24 h, at 37±1° C. Then, by using forceps, suspend the sample for 30 s bythe corner or by one end as appropriate, carefully blot the sample toremove excess fluid, and then weigh it. Repeat the procedure for anothernine samples, in order to obtain statistical significance.

Finally, express the absorptive capacity as the average mass (g) ofsolution retained per 100 cm² (as presented to the wound), per g ofsample or in percentage of the sample weight.

In one embodiment, the at least one silver-release enhancing hydrophiliccomponent of the antimicrobial gel is selected from a group comprisingmono- di- and/or polysaccharides, sugar alcohols, polyols, polyethers,polyesters, polyamides and/or polymers comprising pendant carboxylicacid groups and/or pendant sulphonate groups. In a further embodiment,the at least one silver salt, that mediated the antimicrobial effect, isselected from the group comprising Ag₂SO₄, Ag₂SO₃, AgNO₃, Ag₂CO₃,Ag₃PO₄, silver zirconium, and/or organic silver salts, such as silvercitrate, silver acetate, silver lactate and/or combinations or mixturesthereof.

In additional embodiments, the antimicrobial gel may comprise one ormore excipients selected from the group comprising siloxane-containingcopolymers, siloxane polymer networks, and silica particles.

Microbial inhibition may naturally be carried out using numerousdifferent techniques, for instance through corrected zone of inhibition(CZoI) tests. The antimicrobial gels as per the present invention mayexert an antimicrobial effect, in terms of CZoI, of at least 2 mm at 24h and at least 2 mm at 48 h, and, in yet another embodiment, theaccumulated silver release from the antibacterial gel may amount to atleast 0.3% of the total silver content after 24 h, or may amount to atleast 0.5% of the total silver content after 48 h.

Further as per the aspects and embodiments of the present invention, theat least one (optionally silver release-enhancing) hydrophilic componentmay cause the antimicrobial gels and compositions in accordance with thepresent invention to swell at least 5% (wt/wt) after 24 h in Solution Ain accordance with the free swell absorption method, or it may cause theantimicrobial gels and compositions to swell at least 10% after 72 h inSolution A in accordance with the free swell absorption method.

Thus, another aspect of the present invention pertains to antimicrobialdressings inhibiting microbial growth and comprising the antimicrobialgels of the present invention may be highly useful in various contexts,it may for instance be applied in a professional clinical setting,either by a medical professional or by the patient, or in consumerproduct setting. The antimicrobial dressing may in accordance with anembodiment of the invention relate to any type of dressing with utilityas a substrate for the antimicrobial gel, for instance a wound dressing,an ostomy dressing, ostomy baseplate, incision film, surgical drape, apatch, a bandage, a band-aid, a plaster, an adhesive, an adhesive tape,an adhesive plaster, a sticking-plaster, or a court-plaster, and anycombination thereof.

The antimicrobial gel naturally confers its antimicrobial properties tothe antimicrobial dressings of the present invention, but also thedressing as such can be optimized vis-à-vis for instance shape and/ormorphology from an antimicrobial efficacy perspective. Thus, theantimicrobial dressings of the present invention may be adjusted to suitspecific purposes, both in terms of physical appearance, physicalproperties, as well as in terms of constituents and chemical properties.The silver-releasing properties of the antimicrobial dressings as suchnaturally have a significant impact on the overall antimicrobial effectsseen when utilizing the dressings in for instance a clinical setting.Hence, further in accordance with the invention, the accumulated silverrelease from the antimicrobial dressings of the present invention mayamount to at least 0.3% of the total silver content after 24 h, and atleast 0.5% of the total silver content after 48 h.

The adhesion properties exhibited by the dressings of the presentinvention logically depends on the adhesive properties of theantimicrobial gel comprised in the dressing. Again, the adhesionproperties are naturally highly important both for the actualantimicrobial efficacy and for the patient comfort and compliance. Theantimicrobial dressings of the present invention growth may be highlyuseful in various contexts, it may for instance be applied in aprofessional clinical setting, either by a medical professional or bythe patient, or in consumer product setting.

The antimicrobial gels of the present invention may be prepared using amultitude of methods or combinations of method steps, in accordance withyet another aspect of the present invention, inter alia a methodcomprising an initial step of mixing a first suitable polysiloxane andat least one (silver release-enhancing) hydrophilic component, followedby heating of the obtained mixture until the hydrophilic component ismolten. The mixture obtained after the melting step may then be mixedwith a silver salt and subsequently with a second suitable polysiloxane.Finally, the mixture is cured in the presence of a catalyst, in anembodiment for instance Pt and/or Pd, and/or any other catalyst suitablefor the preparation of antimicrobial gels. In a further embodiment ofthe present invention, the curing may inter alia be carried out atbetween approximately 40 and 140 degrees Centigrade, preferably between60 and 130 degrees. In yet another embodiment, the timeframe duringwhich the curing reaction is carried out may also vary depending on theabove factors, but the crosslinking curing reaction may for instance becarried out for between 5 seconds and 2 hours, preferably between 10seconds and 30 minutes, and more preferably between 30 seconds and 2minutes. Naturally, the above steps may be performed simultaneously orsequentially or in any combination of sequential steps. In yet anotherembodiment of the present invention, the at least one silicone polymernetwork may be mixed with the mixture comprising the first polysiloxaneand the molten release-enhancing hydrophilic component either prior tothe addition of the silver salt or after.

In a further embodiment in accordance with the present invention,methods for preparing the antimicrobial gels may comprise the steps ofmixing at least one alkenyl- and/or alkynyl-substituted polysiloxane, atleast one catalyst, and silica particles, followed by subsequentlyadding silver salt paste to the mixture, forming a component A (FIG. 1).The silver paste may for instance comprise a polymer network and asuitable silver salt, for instance silver sulfate. A B component may beformed through mixing at least one alkenyl- and/or alkynyl-substitutedpolysiloxane, at least one CL comprising silicon-bonded hydrogen atoms,and at least one CE comprising silicon-bonded hydrogen atoms.Thereafter, a silver-release enhancing hydrophilic component is mixedwith the mixture, optionally after heating and/or melting thesilver-release enhancing hydrophilic component. Finally, component A andcomponent B are mixed together prior to coating of a suitable medicalsubstrate, inter alia any type of wound dressing in accordance with thepresent invention, and the preparation is finalized through curing themix into an antimicrobial gel. Naturally, the above steps may beperformed simultaneously or sequentially or in any combination ofsequential steps. The above-described embodiment may be suitable forpreparation of antimicrobial gels and wound dressing on a manufacturingscale, as the process steps are optimized vis-à-vis production settingsand various important process parameters. Prior to curing theantimicrobial gel, said composition may naturally be applied in anypattern, structure, configuration, and/or morphology to a suitablesubstrate, e.g. a wound dressing, in order to further optimize thepreparation process.

In additional embodiments of the present invention, methods forpreparing antimicrobial products, such as antimicrobial gels and/ordressings, may comprise initial preparation of three mixtures, eithersimultaneously or sequentially or in any combination. Said threemixtures may comprise (i) at least one alkenyl- and/oralkynyl-functional polysiloxane, at least one hydrosilylation catalystand, optionally, silica particles, (ii) at least one alkenyl- and/oralkynyl-functional polysiloxane, at least one CE and/or at least one CL,and, optionally, silica particles, and (iii) at least one silver saltand at least one siloxane-containing copolymer. Subsequently, at leastone silver-release enhancing hydrophilic component is mixed with mixture(i) and/or mixture (ii), followed by optionally heating the obtainedmixture(s) to which the silver-release enhancing hydrophilic componentwas added, in order to melt the silver-release enhancing hydrophiliccomponent. The resulting mixtures are thereafter mixed and, afteroptional coating of a suitable substrate, cured, thus creating either anantimicrobial gel and/or an antimicrobial dressing, in accordance withthe present invention.

In further embodiments in accordance with the present invention, themethod for preparing the antimicrobial gels may comprise mixing at leastone alkenyl- and/or alkynyl-substituted polysiloxane, at least onecatalyst, and silica particles, in order to form a component A. Acomponent B may be formed through mixing at least one alkenyl- and/oralkynyl-substituted polysiloxane, at least one CL comprisingsilicon-bonded hydrogen atoms, and at least one CE comprisingsilicon-bonded hydrogen atoms. Further, a silver salt paste may beprepared through mixing a polymer network with a suitable silver salt,for instance silver sulfate. Subsequently, component A is mixed with arelease-enhancing hydrophilic component, and heated if necessary, priorto addition and mixing of the silver paste, and finally addition andmixing of component B, followed by optional coating of a substrate andcuring, in order to form a antimicrobial gel and/or wound dressing inaccordance with the present invention.

In another embodiment of the present invention pertaining to thepreparation of an antimicrobial gel, and an antimicrobial substrate, afirst component is prepared, comprising inter alia an alkenyl- and/oralkynyl-substituted polydiorganosiloxane, a silver salt, silicaparticles, a catalyst, and an inhibitor. Subsequently, said firstcomponent is mixed in a speedmixer until the silica particles have beenthoroughly dispersed, wherein after a second component, comprising analkenyl- and/or alkynyl-substituted polydiorganosiloxane, chainextenders, and crosslinkers, is added, followed by speedmixing andsubsequent application on a suitable substrate. Finally, the substrateand the antimicrobial gel is cured, for instance for approximately 10minutes at 120 degrees, resulting in a product with antimicrobialproperties. As per other embodiments and aspects of the presentinvention, antimicrobial gels may be prepared using numerous additionalconstituents, in order to achieve certain effects pertaining to interalia increased silver release, optimized tack, viscosity, mechanicalstrength, and/or patient comfort and compliance.

The antimicrobial dressings of the present invention may be preparedusing a multitude of methods or combinations of method steps, inter aliaa method comprising, as per an embodiment, an initial step of mixing afirst suitable polysiloxane and at least one hydrophilic component,followed by heating of the obtained mixture until the at least one(optionally silver release-enhancing) hydrophilic component is molten.The mixture obtained after the melting step may then be mixed with asilver salt and subsequently with a second suitable polysiloxane.Thereafter, the mixture may be applied to a substrate, in varioussuitable patterns, morphologies, and thicknesses, followed by curing ofthe substrate and the applied mixture in the presence of a suitablecatalyst, for instance, in an embodiment, Pt and/or Pd, and/or any othersuitable catalyst. In a further embodiment, the curing may inter alia becarried out at between 40 and 140 degrees Centigrade, preferably between60 and 130 degrees. In yet another embodiment, the timeframe duringwhich the curing reaction is carried out may also vary depending on theabove factors, but the crosslinking curing reaction may for instance becarried out for between 5 seconds and 2 hours, preferably between 10seconds and 30 minutes, and more preferably between 30 seconds and 2minutes.

Naturally, the above steps may be performed simultaneously orsequentially or in any combination of sequential steps, for instance maythe mixture, as per an embodiment, be applied to the substrate prior tothe mixing with the second polysiloxane. In a further embodiment, thesubstrate utilized for the preparation of antimicrobial dressings may beany type of dressing with utility as a substrate for the antimicrobialgel, for instance wound dressing, an ostomy dressing, ostomy baseplate,incision film, surgical drape, a pad, a patch, a bandage, a band-aid, aplaster, an adhesive, an adhesive tape, an adhesive plaster, asticking-plaster, or a court-plaster. According to another embodiment,the at least one silicone polymer network may again be mixed with themixture comprising the first polysiloxane and the moltenrelease-enhancing hydrophilic component either prior to the addition ofthe silver salt or after.

In yet another embodiment, antimicrobial dressings are prepared throughinitially heating at least one silver-release enhancing component, atleast one alkenyl- and/or alkynyl-substituted polydiorganosiloxane, atleast one hydrosilylation catalyst, and, optionally, silica particles,followed by mixing of said components, in order to obtain an emulsion.Subsequently, the emulsion is mixed with a silver paste comprising atleast one silver salt and a polysiloxane—polyether copolymer network.Finally, the silver-containing emulsion is blended with a mix of atleast one alkenyl- and/or alkynyl-substituted polydiorganosiloxane andat least one crosslinker polysiloxane comprising silicone-bondedhydrogen, followed by application to a suitable substrate, and curing.

In an additional embodiment in accordance with the present invention,antimicrobial dressings are prepared mixing at least one silver-releaseenhancing hydrophilic component, for instance particles of a suitablesugar alcohol, at least one alkenyl- and/or alkynyl-substitutedpolydiorganosiloxane, and at least one hydrosilylation catalyst, inorder to form a suspension. The suspension if subsequently mixed with asilver paste comprising at least one silver salt and apolysiloxane—polyether copolymer network. Finally, the silver-containingemulsion is blended with a mix of at least one alkenyl- and/oralkynyl-substituted polydiorganosiloxane and at least one crosslinkerpolysiloxane comprising silicone-bonded hydrogen, followed byapplication to a suitable substrate, and curing.

Further as per the present invention, antimicrobial dressings can beprepared through mixing at least one alkenyl- and/or alkynyl-substitutedpolydiorganosiloxane and at least one hydrosilylation catalyst to form acomponent A. Subsequently, at least one alkenyl- and/oralkynyl-substituted polydiorganosiloxane is mixed with a polysiloxanecomprising silicon-bonded hydrogen atoms to form a component B, followedby continuous mixing of components A and B by joining two streamscomprising component A and component B, respectively. A suitable silversalt and additional excipients, for instance a silver-release enhancinghydrophilic component, is subsequently added, inter alia in the form ofa powder. Finally, the obtained mixture is applied to a substrate andcured, in order to generate an antimicrobial dressing as per the presentinvention.

An additional aspect in accordance with the present invention relates touse of the antimicrobial gel in a product for treating wounds, burns,cuts, bruises, and the like, in various settings and for variouspurposes.

It shall be understood that the above described exemplifying embodimentscan be modified without departing from the scope of the invention, interalia with respect to the described constituents, materials, and processparameters applied. The invention will now be further exemplified withthe enclosed examples, which naturally also can be modified withoutdeparting from the scope of the invention.

EXAMPLES

The following materials were used in the preparation of theantimicrobial compositions and gel of the present invention. Vinyl 1000A dimethylvinyl siloxy-terminated polydimethylsiloxane, having aviscosity of 1000 mPa·s containing 0.18-0.26 wt % vinyl, the chainextender trimethylsiloxy-terminated methylhydrogen polydimethylsiloxane,having a viscosity of 25-35 m Pa·s containing 25-30 mol % MeHSiO, andthe crosslinker trimethylsiloxy-terminated methylhydrogenpolydimethylsiloxane having a viscosity of 25-35 m Pa·s containing 25-30mol % as MeHSiO were obtained from ABCR GmbH & Co. KG (AB109358,AB109366, and AB109380 respectively). Platinum catalyst, Cat 511, wasobtained from Hanse Chemie, silica, H15, was obtained from WackerChemie, mannitol was obtained from Sigma Aldrich, Polyethyleneglycol3000 S was obtained from Clariant (referred to as PEG 3000 below),Pluriol 6005 and Pluriol 8005 were obtained from BASF (referred to asPEG 6000 and PEG 8000, respectively), silver sulfate (Ag₂SO₄) wasobtained from Alpha Aesar (stock number 11417), and Velvesil plus andVelvesil 125 were obtained from Momentive.

Example 1 Silicone Gel Compositions

Silicone gel compositions were prepared by mixing together thecomponents in the amounts listed below. First, a silicone gelformulation was prepared, which was utilized together with theantimicrobial and release-enhancing additives.

The silicone gel was prepared in a two-component system in order toseparate the catalyst and the crosslinker/chain extender prior to thecuring process.

Component A may, inter alia, comprise the following components:

-   -   1. Vinyl terminated PDMS (Vin 1000) and Silica (HDK, H15) were        mixed in a jar and blended for 5 minutes with a Speedmixer.    -   2. The catalyst was added and the mixture was blended for 2 min        in the Speedmixer

Component B may, inter alia, comprise the following components:

-   -   1. The polymers, including Vin 1000, CL, and CE, were mixed in a        jar and blended 2 min in the Speedmixer.

TABLE 1 Component A Component B Silica Catalyst CL CE Vin 1000 HDK H15511 Vin 1000 AB 109380 AB 109366 0.479 0.02 0.001 0.197 0.003 0.3 (47.9g) (2 g) (0.1 g) (19.7 g) (0.3 g) (30 g)

Based on the above outlined base formulation, two antimicrobialformulations were prepared.

Example 2 Silicone Formulation with Silver Sulfate and PEG

A formulation was prepared using a method comprising the followingsteps:

-   -   1) Adding a silicone component A (3.75 g), in accordance with        example 1, in a jar with PEG 8000 (3 g).    -   2) heating at 80° C. until the PEG is molten. The phases are        subsequently mixed in a Speedmixer until an emulsion is formed        (a timeframe of approximately 2 min).    -   3) preparing a paste of Ag₂SO₄ (3 g) and Velvesil plus (1.5 g)        by mixing the silver powder and the Velvesil in a jar, and        blending with the Speedmixer.    -   4) adding the silver paste to component A and mix    -   5) adding inhibitor (0.015 g) to silicone B and mix    -   6) add silicone component B (3.75 g)

TABLE 2 PEG 8000 Velvesil Plus Ag₂SO₄ Silicone A Silicone B Inhibitor0.2 0.1 0.2 0.25 0.25 0.001 (3 g) (1.5 g) (3 g) (3.75 g) (3.75 g) (0.015g)

The above outlined steps may naturally, where applicable, be performedsimultaneously or sequentially or in any combination of sequentialsteps.

Example 3 Silicone Formulation with Silver Sulfate and Mannitol

A formulation was prepared using a method comprising the followingsteps:

-   -   1) putting the silicone component A (3 g), in accordance with        example 1, in a jar with mannitol (4.5 g).    -   2) mixing the phases in a Speedmixer until a suspension is        formed (approximately 2 min).    -   3) preparing a paste of Ag₂SO₄ (3 g) and Velvesil plus (1.5 g)        by mixing the silver powder and Velvesil in a jar and blending        with the Speedmixer.    -   4) adding the silver paste to component A and mix    -   5) adding inhibitor (0.015 g) to silicone B and mix    -   6) adding the silicone component B (3.75 g)

TABLE 3 Mannitol Velvesil Plus Ag₂SO₄ Silicone A Silicone B Inhibitor0.3 0.1 0.2 0.2 0.2 0.001 (4.5 g) (1.5 g) (3 g) (3 g) (3 g) (0.015 g)

The formulations were coated on a film substrate comprisingpolyurethane. Test pieces with a diameter of 20 mm were punched andsubjected to antimicrobial testing according to the CZoI method and thetwo-compartment test method.

Example 4 Silicone Formulation with Silver Sulfate and CMC

A formulation was prepared using a method comprising the followingsteps:

-   -   1) putting the silicone component A (5.92 g), in accordance with        example 1, in a jar with CMC Akucell AF 2781W (1.5 g).    -   2) mixing the phases in a Speedmixer until a suspension is        formed (approximately 2 min).    -   3) to component A adding Ag₂SO₄ (1.5 g) and Velvesil plus        (0.15 g) to the mixture and blending with the Speedmixer        (approximately 2 minutes).    -   4) adding the silicone component B (5.92 g) to the mixture and        mix in the speedmixer (approximately 2 minutes).

TABLE 4 CMC Velvesil Plus Ag₂SO₄ Silicone A Silicone B 0.10 0.01 0.100.395 0.395 (1.5 g) (0.15 g) (1.5 g) (5.92 g) (5.92 g)

The formulations were coated on a film substrate comprisingpolyurethane. Test pieces with a diameter of 20 mm were punched andsubjected to antimicrobial testing according to the CZoI method and thetwo-compartment test method.

Example 5 Addition of Silver Sulfate and CMC with the Addition ofSilicone Polyether

-   -   1) To 80 g of component A of silicone gel (Dow Corning 7-9900)        10 g of silver sulfate and 10 g of CMC (Akucell 2781) was added        and blended in a speed mixer for 2 min    -   2) To this mixture 0.2 g of silicone polyether (Dow Corning        FZ 2233) was added and blended in the speed mixer for 2 min    -   3) To this mixture 80 g of component B (Dow corning 7-9900) was        added and blended in the mixer.    -   4) The sample was left to cure at room temperature.

The sample cured to a gel.

Example 6 Addition of Silver Sulfate and CMC with the Addition ofSilicone Polyether Crosspolymer

-   -   1) To 80 g of component A of silicone gel (Dow Corning 7-9900)        10 g of silver sulfate and 10 g of CMC (Akucell 2781) was added        and blended in a speed mixer for 2 min    -   2) To this mixture 1 g of silicone polyether crosspolymer        (Momentive, Velvesil plus) was added and blended in the speed        mixer for 2 min    -   3) To this mixture 80 g of component B (Dow corning 7-9900) was        added and blended in the mixer.    -   4) The sample was left to cure at room temperature.

The sample cured to a gel.

Example 7 Silver Release and Antimicrobial Effects

The antimicrobial effects of the antimicrobial gels of the presentinvention were evaluated for a number of differently formulated gels, assummarized in Table 5 below. Essentially no antimicrobial activity wasdetected when omitting the at least one (optionally silverrelease-enhancing) hydrophilic component (cf. samples 2N1 and 2N2 inTable 5 below). Additionally, hydrophilic components that do not at allenhance the swelling of the antimicrobial products as per the presentinvention analogously cause essentially no antimicrobial effects. Thus,it is clear that the swelling effects mediated by the hydrophiliccomponents as per the present invention result in enhanced antimicrobialefficacy.

TABLE 5 ID 2N1 2N2 3N1 3N6 3N8 5N6 7N4 9N4 9N5 9N8 Ag₂SO₄ 0.1 0.1 0.050.2 0.2 0.2 0.2 0.1 0.1 0.2 PEG 3000 0.1 0.1 0.25 PEG 6000 0.2 PEG 80000.2 Velvesil plus 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Velvesil 125 0.1Mannitol 0.3 0.3 Sorbitol 0.3 PDMS 0.9 0.8 0.75 0.6 0.55 0.5 0.5 0.5 0.50.4 Test results CZoI 24 h (mm) <1 <1 <1 3 5 6 3.5 4 5 6 Total Ag 0 00.7 0.3 16 17 0.03 5 10 34 Release 24 h (%) Total Ag 0 0 0.8 0.8 27 340.07 7.5 12 54 Release 48 h (%)

The antimicrobial gels prepared in accordance with the present inventiondisplayed desirable properties both in terms of silver release over timeand in terms of antimicrobial effects, with the antimicrobial efficacybeing based on measurements of corrected zone of inhibition (CZoI)(Table 4), on the reduction of the number of colony-forming units (CFU)of Pseudomonas aeruginosa only (FIG. 4) and Pseudomonas aeruginosa andStaphylococcus aureus (FIG. 3), and on the modified ISO antimicrobialcontact method. Briefly regarding the data presented in FIGS. 3 and 4,wound dressings comprising composition 5N6 were tested against twocommon infectious agents, i. e. Pseudomonas aeruginosa andStaphylococchus aureus. The samples were inoculated with 10⁶ bacteriaand subjected to substrates coated with antimicrobial compositions ofthe invention. Comparisons of the sample and the control show theantimicrobial effect as log reductions over time, with the antimicrobialgels as per the present invention being able to reduce the number ofcolony forming units (CFUs) of Staphylococcus aureus from 10⁶ to atleast 10⁵ in 24 h, or preferably from 10⁶ to at least 10⁴ in 24 h, ormost preferably from 10⁶ to at least 10³ in 24 h.

FIG. 4 displays data resulting from two-compartment model tests on P.aeruginosa, based on antimicrobial gels in accordance with the presentinvention, comprising excipients such as PEG and mannitol. Substantialantimicrobial effects can be seen with both gels, with at least fourlogs reduction in CFU/ml over time frames as long as one week

Example 8 Swelling Properties

The swelling properties of various antimicrobial gels and cross-linkedcompositions in accordance with the present invention were analyzedusing the free swell absorption method. As can be seen from Table 6, the(optionally silver release-enhancing) hydrophilic components of thepresent invention mediate substantial swelling, leading to improvedsilver release and/or enhanced antimicrobial efficacy.

TABLE 6 Swelling No Sample Description % 6 h % 24 h % 48 h % 72 h 1MAG11-B: 5% Pemulen TR-2 31% 39% 71% 85% 2 MAG11-D: 10% Pemulen 64% 60%73% 72% TR-2 3 MAG11-G: 10% CMC 3281 114% 125% 143% 135% 4 MAG11-H: 20%CMC 3281 279% 326% 353% 360% 5 MAG11-I: 10% Mannitol 53% 62% 69% 67% 6MAG11-J: 20% Mannitol 55% 66% 69% 61% 7 MAG11-K: 10% pestle 38% 66% 74%86% Mannitol

The invention claimed is:
 1. An antimicrobial composition comprising atleast one alkenyl- and/or alkynyl-substituted polysiloxane, at least onepolysiloxane comprising silicon-bonded hydrogen atoms, and at least onehydrosilylation catalyst, wherein the composition further comprises atleast one silver salt and at least one hydrophilic component, whereinthe at least one hydrophilic component promotes release of the at leastone silver salt such that the antimicrobial composition has anaccumulated silver release of at least 0.3% of the total silver contentin the initial antimicrobial composition after 24 hours, and wherein theat least one hydrophilic component makes the antimicrobial composition,when cross-linked, swell at least 5% (wt/wt) after 24 hours in a watersolution containing 8.298 g/L of sodium chloride and 0.368 g/L ofcalcium chloride dihydrate, as measured by the free swell absorptionmethod, wherein the at least one alkenyl- and/or alkynyl-substitutedpolysiloxane is covalently crosslinked to the at least one polysiloxanecomprising silicon-bonded hydrogen atoms, thereby forming anantimicrobial gel.
 2. The antimicrobial composition of claim 1, whereinthe at least one hydrophilic component comprises a glucose, xylitol,sorbitol, mannitol, cyclodextrin, cellulose, hemicellulose,carboxymethylated cellulose, chitosan, dextran, chitin, amylose,amylopectin, polyethylene glycol, polypropylene glycol, copolymer ofpolyethylene glycol and polypropylene glycol, polyglycerol, poly(acrylicacid), copolymer of acrylic acid and C₁₀-C₃₀ alkyl acrylate,poly(acrylamide), maleic anhydride polymer, maleic anhydride copolymer,or carboxy methyl cellulose, methyl cellulose,hydroxymethylpropylcellulose, ethylcellulose, carboxyethylcellulose,hydroxypropylcellulose, hydroxyethylcellulose, carboxymethylcellulose,cellulose alkyl sulfonate, polystyrene sulphonate, vinyl acid, vinylalcohol, or a mixture thereof.
 3. The antimicrobial composition of claim1, wherein the concentration of the at least one hydrophilic componentis between 3% and 40% (w/w).
 4. The antimicrobial composition of claim1, wherein the antimicrobial composition further comprises between 1%and 5% (w/w) silica particles.
 5. The antimicrobial composition of claim1, wherein the silver salt concentration is between 1% and 30% (w/w). 6.The antimicrobial composition of claim 1, wherein the antimicrobialcomposition further comprises at least one siloxane-containingcopolymer.
 7. The antimicrobial composition of claim 6, wherein the atleast one siloxane-containing copolymer comprises at least one siloxanepolymer network, at least one siloxane polyether (SPE), or a mixturethereof.
 8. The antimicrobial composition of claim 6, wherein the atleast one siloxane-containing copolymer is present at a concentration ofbetween 0.1% and 30% (w/w).
 9. The antimicrobial composition of claim 7,wherein the at least one siloxane-containing copolymer is the at leastone siloxane polymer network, wherein the at least one siloxane polymernetwork comprises a poly-ether-siloxane copolymer network.
 10. Theantimicrobial composition according to claim 1, wherein the at least onehydrophilic component comprises a mono-polysaccharide,di-polysaccharide, sugar alcohol, polyol, polyether, polyester,polyamide, polymer comprising a pendant carboxylic acid group, a polymercomprising a pendant sulphonate group, or a mixture thereof.
 11. Theantimicrobial composition of claim 1, wherein the at least one silversalt comprises Ag₂SO₄, Ag₂SO₃; AgNO₃, Ag₂CO₃, Ag₃PO₄, silver zirconium,silver citrate, silver acetate, silver lactate, or a mixture thereof.12. The antimicrobial composition of claim 1, wherein the at least onehydrophilic component comprises a sorbitol, mannitol, polyethyleneglycol, or carboxy methyl cellulose, or a mixture thereof.
 13. Anantimicrobial gel produced from a composition comprising at least onealkenyl- and/or alkynyl-substituted polysiloxane, at least onepolysiloxane comprising silicon-bonded hydrogen atoms, and at least onehydrosilylation catalyst, wherein the composition further comprises atleast one silver salt and at least one hydrophilic component, whereinthe at least one hydrophilic component promotes release of the at leastone silver salt such that the antimicrobial gel has an accumulatedsilver release of at least 0.3% of the total silver content in theinitial antimicrobial gel after 24 hours, and wherein the at least onehydrophilic component makes the antimicrobial composition, whencross-linked, swell at least 5% (wt/wt) after 24 hours in a watersolution containing 8.298 g/L of sodium chloride and 0.368 g/L ofcalcium chloride dihydrate, as measured by the free swell absorptionmethod, wherein the gel is produced through crosslinking the at leastone alkenyl- and/or alkynyl-substituted polysiloxane and the at leastone polysiloxane comprising silicon-bonded hydrogen atoms.
 14. Theantimicrobial gel of claim 13, wherein the crosslinking of thepolysiloxanes is carried out using curing.
 15. The antimicrobial gel ofclaim 13, wherein the antimicrobial gel further comprises one or moreexcipients comprising a siloxane-containing copolymer, silica particle,or a mixture thereof.
 16. The antimicrobial gel of claim 13, wherein thecorrected zone of inhibition (CZoI) of microbial growth brought about bythe antimicrobial gel is at least 2 mm at 24 h.
 17. The antimicrobialgel of claim 13, wherein a circular sample of the antimicrobial gel,assessed using the two-compartment test method, having a diameter ofabout 20 mm and a coat weight of about 500 g/m², when exposed to 4 ml ofbacteria-containing chemical simulated wound fluid at a temperature of37° C., is able to reduce the number of colony forming units (CFUs) ofStaphylococcus aureus from 10⁶ to at least 10⁵ in 24 h.
 18. Theantimicrobial gel of claim 13, wherein the gel has an adhesion withsteel of between 0.1 and 2 N as measured by ASTM Internationals'standard D3330/D3330M-04, method F.
 19. The antimicrobial gel of claim13, wherein the at least one hydrophilic component comprises a glucose,xylitol, sorbitol, mannitol, cyclodextrin, cellulose, hemicellulose,carboxymethylated cellulose, chitosan, dextran, chitin, amylose,amylopectin, polyethylene glycol, polypropylene glycol, copolymer ofpolyethylene glycol and polypropylene glycol, polyglycerol, poly(acrylicacid), copolymer of acrylic acid and C₁₀-C₃₀ alkyl acrylate,poly(acrylamide), maleic anhydride polymer, maleic anhydride copolymer,or carboxy methyl cellulose, methyl cellulose,hydroxymethylpropylcellulose, ethylcellulose, carboxyethylcellulose,hydroxypropylcellulose, hydroxyethylcellulose, carboxymethylcellulose,cellulose alkyl sulfonate, polystyrene sulphonate, vinyl acid, vinylalcohol, or a mixture thereof.
 20. The antimicrobial gel of claim 13,wherein the concentration of the at least one hydrophilic component isbetween 3% and 40% (w/w).
 21. The antimicrobial gel of claim 13, whereinthe antimicrobial gel further comprises between 1% and 5% (w/w) silicaparticles.
 22. The antimicrobial gel of claim 13, wherein the silversalt concentration is between 1% and 30% (w/w).
 23. The antimicrobialgel of claim 13, wherein the antimicrobial gel further comprises atleast one siloxane-containing copolymer.
 24. The antimicrobial gel ofclaim 23, wherein the at least one siloxane-containing copolymercomprises at least one siloxane polymer network, at least one SPE, or amixture thereof.
 25. The antimicrobial gel of claim 23, wherein the atleast one siloxane-containing copolymer is present at a concentration ofbetween 0.1% and 30% (w/w).
 26. The antimicrobial gel of claim 24,wherein the at least one siloxane-containing copolymer is the at leastone siloxane polymer network, wherein the at least one siloxane polymernetwork comprises a poly-ether-siloxane copolymer network.
 27. Theantimicrobial gel according to claim 13, wherein the at least onehydrophilic component comprises a mono-polysaccharide,di-polysaccharide, sugar alcohol, polyol, polyether, polyester,polyamide, polymer comprising a pendant carboxylic acid group, a polymercomprising a pendant sulphonate group, or a mixture thereof.
 28. Theantimicrobial gel of claim 13, wherein the at least one silver saltcomprises Ag₂SO₄, Ag₂SO₃; AgNO₃, Ag₂CO₃, Ag₃PO₄, silver zirconium,silver citrate, silver acetate, silver lactate, or a mixture thereof.29. The antimicrobial composition of claim 13, wherein the at least onehydrophilic component comprises a sorbitol, mannitol, polyethyleneglycol, or carboxy methyl cellulose, or a mixture thereof.
 30. Anantimicrobial dressing comprising the antimicrobial gel of claim
 13. 31.The antimicrobial dressing of claim 30, wherein the antimicrobial gel isapplied on a substrate.
 32. The antimicrobial dressing of claim 30,wherein the dressing comprises a wound dressing, an ostomy dressing,ostomy baseplate, incision film, surgical drape, a patch, a bandage, aband-aid, a plaster, an adhesive, an adhesive tape, an adhesive plaster,a sticking-plaster, a court-plaster, or a combination thereof.
 33. Amethod for preparing an antimicrobial gel of claim 13, comprising thefollowing steps of: (a) preparing the three mixtures (i), (ii), and(iii), either simultaneously or sequentially or in any combination of(i), (ii), and (iii), comprising; (i) at least one alkenyl- and/oralkynyl-functional polysiloxane, at least one hydrosilylation catalystand, optionally, silica particles; (ii) at least one alkenyl- and/oralkynyl-functional polysiloxane, at least one chain extender and/or atleast one crosslinker, and, optionally, silica particles; (iii) at leastone silver salt and at least one siloxane-containing copolymer; (b)mixing at least one hydrophilic component with mixture (i) and/ormixture (ii), followed by optionally heating the mixture(s) to which theat least one hydrophilic component was added, in order to melt the atleast one silver-release enhancing hydrophilic component; (c) mixingmixture (iii) with mixture (i) and/or mixture (ii); (d) mixing mixture(i) and mixture (ii); and (e) curing the mixture obtained in step (d),thereby obtaining the antimicrobial gel.
 34. A method for preparing anantimicrobial dressing of claim 30, comprising the following steps of:(a) preparing the three mixtures (i), (ii), and (iii), eithersimultaneously or sequentially or in any combination of (i), (ii), and(iii), comprising; (i) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one hydrosilylation catalyst and, optionally,silica particles; (ii) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one chain extender and/or at least onecrosslinker, and, optionally, silica particles; (iii) at least onesilver salt and at least one siloxane-containing copolymer; (b) mixingthe at least one hydrophilic component with mixture (i) and/or mixture(ii), followed by optionally heating the mixture(s) to which the atleast one hydrophilic component was added, in order to melt thehydrophilic component; (c) mixing mixture (iii) with mixture (i) and/ormixture (ii) U; (d) mixing mixture (i) and mixture (ii); (e) coating asubstrate with the mixture obtained in step (d); and (f) curing themixture coated on the substrate of step (e), thereby obtaining theantimicrobial dressing.
 35. The method of claim 34, wherein thesubstrate comprises a wound dressing, an ostomy dressing, an ostomybaseplate, an incision film, a surgical drape, a pad, a patch, abandage, a band-aid, a plaster, an adhesive, an adhesive tape, anadhesive plaster, a sticking-plaster, a court-plaster, or a mixturethereof, or wherein the substrate is a component for production of anyone of the above substrates, wherein the component for productioncomprises a film, a textile, a foam, a non-woven film, a fiber network,a knitted fabric, or a combination thereof.
 36. A method for treating aburn, scar, bacterial infection, viral infection, and/or fungalinfection, wherein the method comprises applying the antimicrobial gelof claim 13 to a patient in need thereof.
 37. A method for treating aburn, scar, bacterial infection, viral infection, and/or fungalinfection, wherein the method comprises applying the antimicrobialdressing of claim 30 to a patient in need thereof.
 38. An antimicrobialgel comprising at least two polysiloxanes, wherein the antimicrobial gelis formed by creating at least one covalent bond between at least one analkenyl and/or alkynyl moiety of a first polysiloxane and at least oneSi—H moiety of a second polysiloxane, the antimicrobial gel furthercomprises at least one hydrosilylation catalyst, at least one silversalt, and at least one hydrophilic component, wherein the at least onehydrophilic component promotes release of the at least one silver saltsuch that the antimicrobial gel has an accumulated silver release of atleast 0.3% of the total silver content in the initial antimicrobial gelafter 24 hours, wherein the at least one hydrophilic component makes theantimicrobial gel swell at least 5% (wt/wt) after 24 hours in a watersolution containing 8.298 g/L of sodium chloride and 0.368 g/L ofcalcium chloride dihydrate, as measured by the free swell absorptionmethod.
 39. The antimicrobial gel according to claim 38, wherein the atleast one hydrophilic component comprises a mono-polysaccharide,di-polysaccharide, sugar alcohol, polyol, polyether, polyester,polyamide, polymer comprising a pendant carboxylic acid group, a polymercomprising a pendant sulphonate group, or a mixture thereof.
 40. Theantimicrobial gel of claim 38, wherein the at least one silver saltcomprises Ag₂SO₄, Ag₂SO₃; AgNO₃, Ag₂CO₃, Ag₃PO₄, silver zirconium,silver citrate, silver acetate, silver lactate, or a mixture thereof.41. The antimicrobial gel of claim 38, wherein the antimicrobial gelfurther comprises one or more excipients comprising asiloxane-containing copolymer, silica particle, or a mixture thereof.42. The antimicrobial gel of claim 38, wherein the corrected zone ofinhibition (CZoI) of microbial growth brought about by the antimicrobialgel is at least 2 mm at 24 h.
 43. An antimicrobial dressing comprisingthe antimicrobial gel of claim
 38. 44. The antimicrobial dressing ofclaim 43, wherein the antimicrobial gel is applied on a substrate. 45.The antimicrobial dressing of claim 43, wherein the dressing comprises awound dressing, an ostomy dressing, ostomy baseplate, incision film,surgical drape, a patch, a bandage, a band-aid, a plaster, an adhesive,an adhesive tape, an adhesive plaster, a sticking-plaster, acourt-plaster, or a combination thereof.
 46. A method for preparing anantimicrobial gel of claim 38, comprising the following steps of: (a)preparing the three mixtures (i), (ii), and (iii), either simultaneouslyor sequentially or in any combination of (i), (ii), and (iii),comprising; (i) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one hydrosilylation catalyst and, optionally,silica particles; (ii) at least one alkenyl- and/or alkynyl-functionalpolysiloxane, at least one chain extender and/or at least onecrosslinker, and, optionally, silica particles; (iii) at least onesilver salt and at least one siloxane-containing copolymer; (b) mixingat least one hydrophilic component with mixture (i) and/or mixture (ii),followed by optionally heating the mixture(s) to which the at least onehydrophilic component was added, in order to melt the at least onesilver-release enhancing hydrophilic component; (c) mixing mixture (iii)with mixture (i) and/or mixture (ii); (d) mixing mixture (i) and mixture(ii); and (e) curing the mixture obtained in step (d), thereby obtainingthe antimicrobial gel.
 47. A method for preparing an antimicrobialdressing of claim 43, comprising the following steps of: (a) preparingthe three mixtures (i), (ii), and (iii), either simultaneously orsequentially or in any combination of (i), (ii), and (iii), comprising;(i) at least one alkenyl- and/or alkynyl-functional polysiloxane, atleast one hydrosilylation catalyst and, optionally, silica particles;(ii) at least one alkenyl- and/or alkynyl-functional polysiloxane, atleast one chain extender and/or at least one crosslinker, and,optionally, silica particles; (iii) at least one silver salt and atleast one siloxane-containing copolymer; (b) mixing the at least onehydrophilic component with mixture (i) and/or mixture (ii), followed byoptionally heating the mixture(s) to which the at least one hydrophiliccomponent was added, in order to melt the hydrophilic component; (c)mixing mixture (iii) with mixture (i) and/or mixture (ii) U; (d) mixingmixture (i) and mixture (ii); (e) coating a substrate with the mixtureobtained in step (d); and (f) curing the mixture coated on the substrateof step (e), thereby obtaining the antimicrobial dressing.
 48. Themethod of claim 47, wherein the substrate comprises a wound dressing, anostomy dressing, an ostomy baseplate, an incision film, a surgicaldrape, a pad, a patch, a bandage, a band-aid, a plaster, an adhesive, anadhesive tape, an adhesive plaster, a sticking-plaster, a court-plaster,or a mixture thereof, or wherein the substrate is a component forproduction of any one of the above substrates, wherein the component forproduction comprises a film, a textile, a foam, a non-woven film, afiber network, a knitted fabric, or a combination thereof.
 49. A methodfor treating a burn, scar, bacterial infection, viral infection, and/orfungal infection, wherein the method comprises applying theantimicrobial gel of claim 38 to a patient in need thereof.
 50. A methodfor treating a burn, scar, bacterial infection, viral infection, and/orfungal infection, wherein the method comprises applying theantimicrobial gel according of claim 38 to a patient in need thereof.